Christmas-PLA Anycubic Filament Set (4 pieces).
4 spools, PLA silk, White, Red, Green, Gold, 210-240°C, 55-56°C, 50-250 mm/s
The Anycubic Christmas PLA filament set includes four spools in festive colors: White, Red, Green, and Gold. With a silky sheen and vibrant colors, it is ideal for creative projects during the holidays. The filaments are equipped with intelligent chips that automatically adjust the printer settings, and offer high break resistance as well as easy handling. Compatible with most FDM 3D printers, they enable impressive printing results.
CHF 43.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
The Anycubic Christmas PLA filament set consists of four spools in festive colors: White, Red, Green, and Gold. It is perfect for creative projects during the holidays, such as printing Christmas ornaments and decorations. The silk filaments provide a smooth, shiny surface and vibrant colors that highlight details and give depth to the models. Thanks to the high break resistance and flexibility of the material, smooth printing is ensured, while the intelligent chips in the filaments make operating the Anycubic ACE Pro printer easier. With the ability to adjust printing parameters, you can customize the appearance of your models and achieve different levels of gloss. Use the reusable spools to reduce waste and save costs.
Specifications
| General | |
|---|---|
| Manufacturer | Anycubic |
| Manufacturer Code | IPHSCSD-103-4 |
| Filament Type | PLA Silk |
| Number of Included Spools | 4 |
| Filament Colors | White, Red, Green, Gold |
| Drying | Recommended |
| Drying Conditions | 50-65°C, 6-8 h |
| Compatibility with ACE Pro Multicolor Filament Box | Yes |
| Recommended Nozzle Diameter | 0.4 mm or larger |
| Recommended Nozzle Temperature | 210-240°C |
| Recommended Bed Temperature | 55-56°C |
| Recommended Print Speed | 50-250 mm/s |
| Maximum Print Speed | 8 s |
| Maximum Volumetric Print Speed (Flow Rate) | 12 mm³/s |
| Density | 1.22 g/cm³ |
| MFI | 9 g/10 min (190°C / 2.16 kg) |
| Melting Point | 164°C |
| Vicat Softening Point | 54°C |
| Deflection Temperature Under Load (0.45 MPa) | 53°C |
| Young's Modulus | 2200±200 MPa |
| Tensile Strength | 37±4 MPa |
| Tensile Strength (Z) | 17±4 MPa |
| Elongation at Break | 28±5% |
| Flexural Modulus | 2100±100 MPa |
| Flexural Strength | 2400±160 MPa |
| Impact Strength (Izod) (X-Y) | 24.7±1.8 kJ/m² |
| Impact Strength (Izod) (Z) | 8±1.1 kJ/m² |