Sunlu PLA Matte Filament 1.75mm 1kg Light Green
1.75 mm diameter ±0.02 mm, 1 kg spool / 330 m length, Matte light green surface, Biodegradable corn-based, Tensile strength 50.5 MPa
Sunlu matte PLA filament in light green with 1.75 mm diameter and 1 kg spool content (approximately 330 m). The matte surface reduces visible layer lines and ensures a uniform print appearance. Based on starch-based plant material and is biodegradable.
CHF30.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA M SG is a matte PLA filament that, through its matte surface structure, makes layer lines less visible and thus creates a cleaner, quieter appearance of printed objects. The material is based on starch-based plant material from maize and is biodegradable.
With a diameter of 1.75 mm and a tight tolerance of ±0.02 mm, the filament can be processed with dimensional accuracy. The melting temperature is around 162.6 °C, the Vicat softening point is 54 °C and the heat deflection temperature is 53 °C. With a tensile strength of 50.5 MPa, a flexural strength of 61 MPa and a flexural modulus of 2234 MPa, the material is suitable for mechanically stressed parts as well as for detailed models.
The filament is compatible with FDM 3D printers with heated bed as well as with 3D printing pens and is aimed at all those seeking a versatile PLA with matte appearance.
Specifications
| General | |
|---|---|
| Color | Light green |
| Technical data | |
| Filament diameter | 1.75 mm |
| Diameter tolerance | ±0.02 mm |
| Spool content | 1 kg |
| Filament length | 330 m |
| Density | 1.3 g/cm³ |
| Vicat softening point | 54 °C |
| Heat deflection temperature | 53 °C |
| Melting temperature | 162.6 °C |
| Melt flow rate | 10.0 ± 0.2 g/10min |
| Tensile strength | 50.5 MPa |
| Elongation at break | 9.6 % |
| Flexural strength | 61 MPa |
| Flexural modulus | 2234 MPa |
| Impact resistance | 4.9 kJ/m² |
| Compatibility | |
| Compatibility | FDM 3D printers with heated bed and 3D printing pens |
| Material | |
| Material | PLA (matte) |
| Raw material base | Starch-based plant material (maize), biodegradable |