Sunlu PLA Matte Filament 1.75 mm White 1 kg
Diameter 1.75 mm, 330 m per spool / 1 kg, Biodegradable PLA, Tolerance ±0.02 mm, For printers & printing pens
Matte PLA filament from Sunlu in white with a diameter of 1.75 mm and a fill weight of 1 kg per spool. Made from renewable, starch-based plant raw materials from corn and biodegradable. Suitable for FDM 3D printers with heated print bed and for 3D printing pens.
CHF31.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA M W is a matte PLA filament in white, made from renewable, starch-based plant raw materials from corn and biodegradable. The matte surface structure provides a subtle, non-glossy finish for printed parts.
With a diameter of 1.75 mm and a tight tolerance of ±0.02 mm at a density of 1.3 g/cm³, the material is designed for uniform material flow. The melting temperature is 162.6 °C, the Vicat softening temperature is 54 °C, and the heat distortion temperature is 53 °C. Mechanically, the filament exhibits a tensile strength of 50.5 MPa, an elongation at break of 9.6%, a flexural strength of 61 MPa, a flexural modulus of 2234 MPa, and an impact resistance of 4.9 kJ/m².
One spool contains 330 m of filament with a fill weight of 1 kg. The material is compatible with FDM 3D printers with heated print bed and with 3D printing pens.
Specifications
| General | |
|---|---|
| Color | White |
| Technical data | |
| Filament diameter | 1.75 mm |
| Diameter tolerance | ±0.02 mm |
| Filament length per spool | 330 m |
| Fill weight | 1 kg |
| Density | 1.3 g/cm³ |
| Vicat softening temperature | 54 °C |
| Heat distortion temperature | 53 °C |
| Melting temperature | 162.6 °C |
| Melt flow rate | 10.0 ± 0.2 g/10min |
| Tensile strength | 50.5 MPa |
| Elongation at break | 9.6 % |
| Flexural strength | 61 MPa |
| Flexural modulus | 2234 MPa |
| Impact resistance (notch) | 4.9 kJ/m² |
| Compatibility | |
| Compatibility | FDM 3D printers with heated print bed and 3D printing pens |
| Material | |
| Material | PLA (matte) |
| Raw material base | Renewable starch-based plant raw materials (corn) |
| Biodegradable | Yes |
More Information
| Material | PLA (matte) |
|---|