Sunlu PLA+ Filament 1.75 mm Black
Diameter 1.75 mm, Dimensional accuracy ±0.02 mm, Tensile strength 64 MPa, Flexural strength 86 MPa, Print temperature 195–220 °C
Sunlu PLA+ is a 1.75 mm filament in black with high dimensional accuracy of ±0.02 mm. It offers good mechanical properties such as tensile strength and impact resistance, and is compatible with common FDM printers.
CHF31.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA+ is a 1.75 mm filament in black for FDM 3D printers, including devices from Bambu Lab, Creality, Prusa, and Anycubic. With a density of 1.23 g/cm³ and dimensional accuracy of ±0.02 mm, it ensures uniform material supply for consistent printing results at temperatures of 195–220 °C and speeds between 50 and 300 mm/s.
Mechanically, the material exhibits a tensile strength of 64 MPa, a flexural strength of 86 MPa, and a flexural modulus of 2907 MPa, with an elongation at break of 17% and an Izod impact strength of 3.5 kJ/m². The Vicat softening point is 54 °C, the heat deflection temperature is 53 °C, and the melting temperature is 164 °C, with a melt flow rate of 6.3 g/10min. These properties make the filament suitable for both functional components and detailed models.
Specifications
| General | |
|---|---|
| Manufacturer | Sunlu |
| Model | PLA+ B |
| Color | Black |
| Technical data | |
| Filament diameter | 1.75 mm |
| Dimensional accuracy | ±0.02 mm |
| Melt flow rate | 6.3 g/10min |
| Print speed | 50–300 mm/s |
| Print temperature | 195–220 °C |
| Compatibility | |
| Compatible printers | FDM 3D printers (e.g. Bambu Lab, Creality, Prusa, Anycubic) |
| Material | |
| Density | 1.23 g/cm³ |
| Vicat softening point | 54 °C |
| Heat deflection temperature (HDT) | 53 °C |
| Melting temperature | 164 °C |
| Tensile strength | 64 MPa |
| Elongation at break | 17 % |
| Flexural strength | 86 MPa |
| Flexural modulus | 2907 MPa |
| Izod impact strength (X-Y) | 3.5 kJ/m² |