Diameter 1.75 mm (±0.02 mm), Print speed up to 300 mm/s, Tensile strength 53.4 MPa, Flexural strength 81.8 MPa, Compatible with almost all FDM printers
Sunlu PLA+ 2.0 is a black 3D printing filament with a diameter of 1.75 mm and ±0.02 mm tolerance. It supports print speeds up to 300 mm/s and offers higher tensile strength and impact resistance compared to standard PLA. Suitable for almost all FDM 3D printers.
CHF29.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA+ 2.0 is a PLA filament with a diameter of 1.75 mm and a tight tolerance of ±0.02 mm, which supports uniform extrusion. With a melt flow rate of 7.8 g/10 min and a melting temperature of 164 °C, the material is designed for uniform material flow and allows print speeds up to 300 mm/s.
Mechanically, the material exhibits a tensile strength of 53.4 MPa, a flexural strength of 81.8 MPa, and a flexural modulus of 2740 MPa, with an elongation at break of 20.3 %. The IZOD impact strength is 19.8 kJ/m². The Vicat softening temperature is 54 °C, the heat deflection temperature is 53.8 °C, with a density of 1.21 g/cm³.
The filament is compatible with SUNLU devices as well as almost all other FDM 3D printers, making it suitable for a wide range of printers and applications.
Specifications
| Technical data | |
|---|---|
| Diameter | 1.75 mm |
| Diameter Tolerance | 0.02 mm |
| Maximum Print Speed | 300 mm/s |
| Density | 1.21 g/cm³ |
| Vicat Softening Temperature | 54 °C |
| Heat Deflection Temperature (HDT) | 53.8 °C |
| Melting Temperature | 164 °C |
| Melt Flow Rate | 7.8 g/10min |
| Tensile Strength | 53.4 MPa |
| Elongation at Break | 20.3 % |
| Flexural Strength | 81.8 MPa |
| Flexural Modulus | 2740 MPa |
| IZOD Impact Strength | 19.8 kJ/m² |
| Compatibility | |
| Compatibility | SUNLU devices as well as almost all other FDM 3D printers |
| Material | |
| Color | Black |
| Material | PLA+ |