Sunlu PLA+ 2.0 Filament 1.75 mm Red
Diameter 1.75 mm (±0.02 mm), Print speed up to 300 mm/s, Tensile strength 53.4 MPa, IZOD impact strength 19.8 kJ/m², Compatible with FDM 3D printers
Sunlu PLA+ 2.0 is a PLA+ filament with 1.75 mm diameter and ±0.02 mm tolerance for FDM 3D printers. It enables print speeds up to 300 mm/s with stable material feeding. Thanks to high tensile strength and impact resistance, it is suitable for robust and functional parts.
CHF31.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA+ 2.0 in red is a PLA+ filament with a diameter of 1.75 mm and a tight tolerance of ±0.02 mm, which promotes uniform extrusion and precise print results. With a melt flow rate of 7.8 g/10min, rapid material feeding is possible, which supports print speeds of up to 300 mm/s.
The mechanical values of the material – a tensile strength of 53.4 MPa, a flexural strength of 81.8 MPa, and an IZOD impact strength of 19.8 kJ/m² – speak to parts that must also withstand mechanical loads. The Vicat softening temperature is 54 °C, the heat deflection temperature is 53.8 °C, and the melting temperature is 164 °C.
With a density of 1.21 g/cm³, the filament is compatible with common FDM 3D printers and can be used for various models and functional parts.
Specifications
| General | |
|---|---|
| Color | Red |
| Technical data | |
| Diameter | 1.75 mm |
| Diameter tolerance | ±0.02 mm |
| Maximum print speed | 300 mm/s |
| Density | 1.21 g/cm³ |
| Vicat softening temperature | 54 °C |
| Heat deflection temperature (HDT) | 53.8 °C |
| Melting temperature | 164 °C |
| Melt flow rate | 7.8 g/10min |
| Tensile strength | 53.4 MPa |
| Elongation at break | 20.3 % |
| Flexural strength | 81.8 MPa |
| Flexural modulus | 2740 MPa |
| IZOD impact strength | 19.8 kJ/m² |
| Compatibility | |
| Compatibility | FDM 3D printers |
| Material | |
| Material | PLA+ |
More Information