Sunlu PLA+ 2.0 3D Printer Filament 1.75mm Ivory
1.75 mm diameter ±0.02 mm, Print speed up to 300 mm/s, Tensile strength 53.4 MPa, Flexural strength 81.8 MPa, Wide printer compatibility
Sunlu PLA+ 2.0 is a 3D printer filament with a diameter of 1.75 mm in ivory color. It supports print speeds up to 300 mm/s and is compatible with Sunlu devices as well as virtually all FDM 3D printers from other manufacturers.
CHF31.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
Sunlu PLA+ 2.0 is a PLA filament for FDM 3D printers with a diameter of 1.75 mm and a tight tolerance of ±0.02 mm, which promotes uniform extrusion and precise prints. With a density of 1.21 g/cm³, a melt flow rate of 7.8 g/10min and a melting temperature of 164 °C, the material can be processed at print speeds of up to 300 mm/s.
Mechanically, the filament exhibits a tensile strength of 53.4 MPa, a flexural strength of 81.8 MPa with a flexural modulus of 2740 MPa, an elongation at break of 20.3 % as well as an Izod impact strength of 19.8 kJ/m². The Vicat softening temperature is 54 °C, the heat deflection temperature is 53.8 °C. It is suitable for Sunlu devices and is also compatible with virtually all FDM 3D printers from other manufacturers.
Specifications
| General | |
|---|---|
| Color | Ivory |
| Technical data | |
| Filament diameter | 1.75 mm |
| Diameter tolerance | ±0.02 mm |
| Maximum print speed | 300 mm/s |
| Density | 1.21 g/cm³ |
| Vicat softening temperature | 54 °C |
| Heat deflection temperature | 53.8 °C |
| Melting temperature | 164 °C |
| Melt flow rate | 7.8 g/10min |
| Tensile strength | 53.4 MPa |
| Elongation at break | 20.3 % |
| Flexural strength | 81.8 MPa |
| Flexural modulus | 2740 MPa |
| Izod impact strength | 19.8 kJ/m² |
| Compatibility | |
| Compatibility | Sunlu devices and virtually all FDM 3D printers from other manufacturers |