Sunlu PLA+ 2.0 Filament (Oak)
1.75 mm, oak, 1.21 g/cm³, 54 °C, 300 mm/s
The Sunlu PLA+ 2.0 Filament in Oak offers high reliability and a smooth printing process with up to 1.5 times higher flow than standard PLA. It is crack-resistant and durable, ideal for robust models and functional parts. With a printing speed of up to 300 mm/s and wide compatibility with FDM 3D printers, it is the perfect choice for fast and precise printing projects.
CHF 29.95
Incl. VAT and recycling fee
More than 10 available
- Free shipping with Swiss Post
- Us de Bärge – shipped from Thusis
- 60 days free returns
- Price match guarantee
Description
The Sunlu PLA+ 2.0 Filament in Oak is a high-quality 3D printing material designed for users who value reliability and quality. With a flow rate up to 1.5 times higher than conventional PLA, it enables a stable printing process and minimizes the risk of extrusion problems. The combination of user-friendliness and durability, comparable to Easy ABS, makes it ideal for applications where resilience and a long lifespan are crucial. Furthermore, the filament supports printing speeds of up to 300 mm/s, allowing for a significant acceleration of production times without compromising print quality. With a diameter of 1.75 mm and a tolerance of ±0.02 mm, it ensures precise results and is thus the perfect choice for both everyday and more demanding projects.
Specifications
| General | |
|---|---|
| Manufacturer | Sunlu |
| Model | PLA+ 2.0 Oak |
| Color | Oak |
| Density | 1.21 g/cm³ |
| Vicat softening temperature | 54 °C |
| Heat deflection temperature (HDT) | 53.8 °C |
| Melting temperature | 164 °C |
| Melt flow rate | 7.8 g/10 min |
| Tensile strength | 53.4 MPa |
| Elongation at break | 20.3 % |
| Flexural strength | 81.8 MPa |
| Flexural modulus | 2740 MPa |
| IZOD notched impact strength | 19.8 kJ/m² |